Paramagnetic Defects and Thermoluminescence in Irradiated Nanostructured Monoclinic Zirconium Dioxide
Date
2022
Authors
Ananchenko, Daria V.
Nikiforov, Sergey V.
Sobyanin, Konstantin V.
Konev, Sergey F.
Dauletbekova, Alma K.
Akhmetova-Abdik, Gulzhanat
Akilbekov, Abdirash T.
Popov, Anatoli I.
Journal Title
Journal ISSN
Volume Title
Publisher
MDPI
Abstract
The ESR spectra of nanostructured samples of monoclinic ZrO2 irradiated by electrons with energies of 130 keV, 10 MeV, and by a beam of Xe ions (220 MeV) have been studied. It has been established that irradiation of samples with electrons (10 MeV) and ions leads to the formation of radiation-induced F+ centers in them. Thermal destruction of these centers is observed in the temperature range of 375–550 K for electron-irradiated and 500–700 K for ion-irradiated samples. It is shown that the decrease in the concentration of F+ centers is associated with the emptying of traps responsible for thermoluminescence (TL) peaks in the specified temperature range. In the samples irradiated with an ion beam, previously unidentified paramagnetic centers with g = 1.963 and 1.986 were found, the formation of which is likely to involve Zr3+ ions and oxygen vacancies. Thermal destruction of these centers occurs in the temperature range from 500 to 873 K. © 2022 by the authors. --//-- This is an open access article Ananchenko D.V., Nikiforov S.V., Sobyanin K.V., Konev S.F., Dauletbekova A.K., Akhmetova-Abdik G., Akilbekov A.T., Popov A.I., "Paramagnetic Defects and Thermoluminescence in Irradiated Nanostructured Monoclinic Zirconium Dioxide", (2022) Materials, 15 (23), art. no. 8624, DOI: 10.3390/ma15238624 published under the CC BY 4.0 licence.
Description
The work was carried out under the grant of the Ministry of Education and Science of the Republic of Kazakhstan AP09260057, “Luminescence and radiation resistance of synthesized under different conditions micro- and nanostructured compacts and ceramics based on ZrO2”. The research was partly (A.I.P.) performed at the Center of Excellence of the Institute of Solid State Physics, University of Latvia, supported through European Union Horizon 2020 Framework Programme H2020-WIDESPREAD-01-2016-2017-TeamingPhase2, under grant agreement No. 739508, project CAMART2.
Keywords
Research Subject Categories::NATURAL SCIENCES::Physics , electron irradiation , F+ centers , ion irradiation , paramagnetic defects , zirconium dioxide